Improved coating systems, use thereof for coating components and components coated therewith for rail vehicles and aircrafts

ABSTRACT

A coating material for producing a coating includes 15 to 70 wt. % of at least one CH acidic compound, 4 to 40 wt. % of at least one vinylogous carbonyl compound, 0.1 to 15 wt. % of at least one latent-basic catalyst, 0.00001 to 10 wt. % of at least one light stabilizer, 0.00001 to 20 wt. % of at least one open time extender, and 0.00001 to 20 wt. % of at least one pot life extender. Each wt. % of a respective ingredient is based on a total amount of the coating material.

CROSS REFERENCE TO PRIOR APPLICATIONS

This application is a U.S. National Phase application under 35 U.S.C. § 371 of International Application No. PCT/DE2016/000164, filed on Apr. 20, 2016 and which claims benefit to German Patent Application No. 10 2015 105 987.8, filed on Apr. 20, 2015. The International Application was published in German on Oct. 27, 2016 as WO 2016/169543 A1 under PCT Article 21(2).

FIELD

The present invention relates to improved coating materials based on RMA systems which cross-link with the aid of a classic Michael addition. The present invention also relates to coatings produced therefrom and coated components, in particular to components for rail vehicles and aircraft, for example, railway cars or air planes.

Coating materials which cross-link in a Michael addition reaction have previously been described. The coatings produced therefrom have high weathering stability and chemical resistances. The rapid curing of these coating materials is achieved by the use of high catalyst content, wherein, however, the processing time or the pot life of the coating material is strongly reduced.

Rapid curing is particularly advantageous primarily in the case of coating or painting large components, for example, airplanes or railway cars. However, merely due to the size of the surfaces, a relatively long time is required for coating the entire component so that the coating materials used must have long pot lives and long open times. In the following, “pot life” is designated as the time interval between mixing all components of a coating material and the time at which the cross-linking reaction in the coating material has progressed to the extent that the coating material may no longer be processed. In the following, “open time” is designated as the time interval in which a coating material film applied to a surface may be corrected without impairing the gradient properties.

During application of the coating material, the already coated areas must additionally be able to absorb the overspray that occurs during painting of the adjacent areas, without surface defects forming, for example, due to a poor progression. In the following, “overspray” is designated as the material loss of the coating material caused during spray painting. The material loss may be caused by spraying past caused by an unfavorable orientation of the spray gun toward the workpiece or by strongly interrupted workpieces, such as grids. Overspray may also occur due to coating material drops flowing off laterally in front of the workpiece surfaces. Overspray absorption is thereby the property of an applied coating material to absorb material from an overspray so that the desired smooth surface of the film or coating is retained.

A very fast drying or curing is desired for the coating after application of the coating material as a film or layer on a substrate surface. Forced drying at increased temperature is generally not possible for large components, as correspondingly large ovens would be required therefor. Fast drying at room temperature is therefore particularly desirable primarily for coating or painting very large components.

Binder systems cross-linking in a Michael addition, designated hereafter as “RMA systems”, are described in EP 2374836 A1 and have a favorable ratio of pot life to drying time. The described binder systems show short drying times with long pot lives even at room temperature. Reference is thus specifically made to EP 2374836 A1 as a part of the description of the present invention. The disadvantage of known RMA systems is that the coating materials and coatings produced therefrom do not show the necessary and conventional properties.

SUMMARY

An aspect of the present invention is to provide improved coating materials, coatings, and coating systems based on RMA systems which are particularly suitable for coating components of aircraft and rail vehicles.

In an embodiment, the present invention provides a coating material for producing a coating which includes 15 to 70 wt. % of at least one CH acidic compound, 4 to 40 wt. % of at least one vinylogous carbonyl compound, 0.1 to 15 wt. % of at least one latent-basic catalyst, 0.00001 to 10 wt. % of at least one light stabilizer, 0.00001 to 20 wt. % of at least one open time extender, and 0.00001 to 20 wt. % of at least one pot life extender. Each wt. % of a respective ingredient is based on a total amount of the coating material.

DETAILED DESCRIPTION

The coating materials according to the present invention comprise at least one RMA system which has one or more CH acidic compounds A, one or more vinylogous carbonyl compounds B, one or more latent-basic catalysts C, one or more light stabilizers, one or more pot life extenders, and one or more open time extenders.

In the following, the expression “light stabilizer” is understood to refer to additives and adjuvants that protect coatings from the influence of UV light, in particular additives and adjuvants that prevent or at least significantly delay polymer degradation caused by UV radiation. The expression “pot life extenders” is understood to refer to additives and adjuvants which, as components of the ready to be used mixed coating material, delay the curing of the coating material prior to application. Pot life extenders evaporate during application so that the curing of the applied coating material is not affected, in particular, is not extended. The expression “open time extenders” is understood to refer to additives and adjuvants which also remain in the coating material after application and delay curing for the coating.

The coating materials according to the present invention contain at least:

-   -   15 to 70, for example, 20 to 60, for example, 25 to 55 wt. % CH         acidic compounds A;     -   4 to 40, for example, 8 to 35, for example, 10 to 30 wt. %         vinylogous carbonyl compounds B;     -   0.1 to 15, for example, 0.2 to 10, for example, 0.3 to 5 wt. %         latent-basic catalysts C;     -   0.00001 to 10, for example, 0.5 to 5, for example, 1 to 3 wt. %         light stabilizers;     -   0.00001 to 20, for example, 0.01 to 10, for example, 0.1 to 5         wt. % open time extenders;     -   0.00001 to 20, for example, 0.01 to 15, for example, 0.1 to 10         wt. % pot life extenders;     -   0 to 70, for example, 0.00001 to 65, for example, 0.00001 to 40         wt. % pigments;     -   0 to 25, for example, 0.00001 to 8, for example, 0.00001 to 5         wt. % dispersing additives;     -   0 to 60, for example, 0.00001 to 40, for example, 0.00001 to 30         wt. % functional fillers; and     -   0 to 50, for example, 0.00001 to 40, for example, 0.00001 to 30         wt. % aprotic solvents,

wherein, the indicated amounts respectively relate to the total amount of the coating material.

According to the present invention, the compounds A and B are used in a molar ratio A:B of 0.5:1 to 2:1, for example, of 0.75:1 to 1.6:1, for example, of 0.9:1 to 1.3:1, for example, of 0.95:1 to 1.1:1, wherein the molar amounts refer to the acidic protons of the compounds A and to the vinylogous carbonyl groups of the compounds B.

According to the present invention, the catalysts C and compounds A are used in a molar ratio C:A of 0.8:1 to 2.5:1, for example, 1.1:1 to 1.9:1, for example, 1.3:1 to 1.7:1, wherein the molar amounts refer to the cation X⁺ of catalyst C and the acidic protons of the compounds A.

Suitable CH acidic compounds A are compounds with the general Formula I

wherein,

-   -   R is hydrogen, an alkyl radical, or an aryl radical, and     -   Y, Y′ are alkyl radicals, aralkyl radicals, aryl radicals,         alkoxy radicals or amino groups, for example, primary amino         groups, and Y and Y′ may be the same or different.

Furthermore, the —C(═O)—Y and/or —C(═O)—Y′ groups from Formula I may be replaced by CN— or aryl groups.

According to the present invention, malonic acid esters, acetoacetic acid esters, or mixtures thereof can, for example, be used. Malonic acid esters can, for example, be used with oligomer and polymer substituents, for example, based on polyesters, polyurethanes, polyacrylates, epoxy resins, polyamides, or polycarbonates. Malonic acid esters can for example, be used with oligomer and polymer substituents based on polyesters, polyurethanes, and/or polycarbonates. Acetoacetic acid esters can, for example, be used which contain oligomer and polymer substituents, for example, based on polyalcohols, polyvinyl alcohols, epoxy resins, hydroxy-functional polyethers, polyesters, or polyacrylates. Acetoacetic acid esters can, for example, be used with oligomer and polymer substituents based on polyesters and/or polyacrylates. Compounds selected from the group containing malonic acid esters with oligomer and polymer substituents based on polyesters, which are obtained from the reaction of at least malonic acid, malonic acid dimethyl ester, and/or malonic acid diethyl ester with hexahydrophthalic acid and/or its anhydride and neopentyl glycol, and acetoacetic acid esters with oligomer and polymer substituents based on polyesters, which are obtained from the reaction of at least acetoacetic acid, acetoacetic acid methyl ester, and/or acetoacetic acid ethyl ester with hexahydrophthalic acid and/or its anhydride and neopentyl glycol can, for example, be used.

Suitable vinylogous carbonyl compounds B are, for example, acrylates and/or maleates, for example, unsaturated acryloyl-functional compounds. According to the present invention, acrylesters can, for example, be used that are made from compounds containing 1 to 20 carbon atoms and at least 2, for example, 2 to 6 hydroxyl groups. According to the present invention, polyesters can, for example, be used that are obtained from reacting maleic acid, fumaric acid, and/or itaconic acid, or anhydrides thereof with di- or polyvalent hydroxyl compounds which may contain a monovalent hydroxyl- or carboxyl compound. Resins can, for example, be used, for example polyesters, polyurethanes, polyethers, and/or alkyd resins which correspondingly contain activated unsaturated groups, for example, urethane acrylates, polyether acrylates, polyfunctional polyacrylates, polyalkylmaleates, and polyacrylates that are obtained from the reaction of acrylic acid with epoxy resins. According to the present invention, butanediol diacrylate, hexanediol diacrylate, trimethylolpropane triacrylate, entaerythritol tetraacrylate, di(trimethylolpropane)tetraacrylate, dipentaerythritol hexaacrylate, dipropylene glycol diacrylate, and tripropylene glycol diacrylate can, for example, be used.

Suitable latent-basic compounds for the catalysts C are, for example, substituted carboxylic acid salts of Formula II:

wherein,

-   -   R is hydrogen, an alkyl or aralkyl (Ar—R), or a polymer,     -   X⁺ is an alkali earth metal cation or an alkaline earth metal         cation, for example, lithium, sodium, or potassium,         -   or a quaternary ammonium or phosphonium salt of the formula             (R′)₄Y⁺, where,         -   Y is nitrogen or phosphorus,         -   R′ is the same or different, is hydrogen, an alkyl-, aral-,             or aralkyl radical, or a polymer,         -   and where,         -   R and R′ may form a ring structure,         -   or,         -   R and R′ may be a polymer.

According to the present invention, R can, for example, be an alkyl group or an aralkyl group, for example, an alkyl group with 1 to 4 carbon atoms. The carbonate group and the cation X⁺ may also additionally be present on a molecule with the corresponding structure. Furthermore, R′ can, for example, be an alkyl group, for example, an alkyl group with 1 to 4 carbon atoms, for example, with 3 to 4 carbon atoms. According to the present invention, ammonium- and/or phosphonium carbonate can, for example, be used. Suitable ammonium carbonates are, for example, tetrahexylammonium methyl carbonate, tetrahexylammonium hydrogen carbonate, tetradecanyl trihexylammonium methyl carbonate, tetradecylammonium methyl carbonate, tetrabutylammonium methyl carbonate, tetrabutylammonium ethyl carbonate, tetrabutylammonium hydrogen carbonate, tetrapropylammonium methyl carbonate, tetrapropylammonium ethyl carbonate, tetrapropylammonium hydrogen carbonate, benzyltrimethylammonium methyl carbonate, trihexylmethylammonium methyl carbonate, or trioctylmethylammonium methyl carbonate. Tetrabutylammonium methyl carbonate, tetrabutylammonium ethyl carbonate, tetrabutylammonium hydrogen carbonate, tetrapropylammonium methyl carbonate, tetrapropylammonium ethyl carbonate, tetrapropylammonium hydrogen carbonate, and mixtures thereof can, for example, be used.

Suitable light stabilizers are radical scavengers such as sterically inhibited aliphatic amines, for example, based on substituted 2,2,6,6-tetramethylpiperidines, UV absorbers such as 2-hydroxyphenyl benzotriazoles, 2-hydroxybenzophenones, 2-hydroxyphenyltriazines, or oxalanilides, and quenchers such as organic nickel compounds and peroxide decomposers such as thioethers or phosphites. Radical scavengers, for example, sterically inhibited aliphatic amines based on substituted 2,2,6,6-tetramethylpiperidines, and/or UV absorbers, for example, 2-hydroxyphenyl benzotriazoles, 2-hydroxybenzophenones, 2-hydroxyphenyltriazines, and oxalanilides can, for example, be used. Substituted 2,2,6,6-tetramethylpiperidines, 2-hydroxyphenyltriazines, 2-hydroxybenzophenones, and mixtures thereof can, for example, be used.

Suitable pot life extenders are short-chain alcohols which have an evaporation number below 35, for example, below 20. Alcohols with up to 6 carbon atoms, for example, up to 4, for example, up to 3, are particularly suitable. Thus, for example, methanol, ethanol, n-propanol, i-propanol, n-butanol, i-butanol, and mixtures thereof can, for example, be used according to the present invention.

Suitable open time extenders are basic NH-functional compounds with a pK_(a) value between 4 and 14. Succinimides, 1,2,4,-triazoles, 1,2,3,-benzotriazoles, 5,5-diphenylhydantoins, hydantoins, (RS)-3-ethyl-3-methylpyrrolidine-2,5-dione, and mixtures thereof can, for example, be used. Succinimides, 1,2,4,-triazoles, 1,2,3,-benzotriazoles, and mixtures thereof can, for example, be used.

In an embodiment of the present invention, inorganic and/or organic pigments can, for example, be added to the coating materials to produce a color-producing coating. Additional additives, such as dispersing additives and functional fillers, may also be added in order to improve the required properties of the coating material and/or of the coating.

Inorganic and/or organic pigments may be added to the coating materials according to the present invention in amounts up to 70, for example, 0.00001 to 65, for example, 0.00001 to 40 wt. %, wherein the indicated amounts respectively relate to the total amount of the coating material. Suitable inorganic pigments are, for example, titanium dioxide, iron oxides, chromium oxides, chromium titanates, bismuth vanadate, cobalt blue, and carbon blacks. Titanium dioxide, iron oxides, and carbon blacks can, for example, be used as inorganic pigments. Suitable organic pigments are, for example, pigment yellow 151, pigment yellow 213, pigment yellow 83, pigment orange 67, pigment orange 62, pigment orange 36, pigment red 170, pigment violet 19, pigment violet 23, pigment blue 15:3, pigment blue 15:6, pigment green 7. Pigment yellow 151, pigment orange 67, pigment red 170, pigment violet 19, pigment blue 15:3, and pigment green 7 can, for example, be used.

In an embodiment, the coating materials may additionally contain up to 25, for example, 0.00001 to 8, for example, 0.00001 to 5 wt. % dispersing agents, wherein the indicated amounts respectively relate to the total amount of the coating material. Suitable dispersing agents are, for example, high molecular weight block copolymers with pigment affinic groups, highly branched polyesters, and acrylate polyester copolymers with pigment affinic groups. High molecular weight block copolymers with pigment affinic groups can, for example, be used as dispersing additives.

In an embodiment, the coating materials may additionally contain up to 60, for example, 0.00001 to 50, for example, 0.00001 to 40 wt. % functional fillers, wherein the indicated amounts respectively relate to the total amount of the coating material. Suitable fillers can, for example, be carbonates such as chalk, limestone, calcite, precipitated calcium carbonate, dolomite, barium carbonate, sulfates such as barite, blanc fixe, calcium sulfate, silicates such as talc, pyrophyllite, chlorite, hornblende, mica, china clay, wollastonite, powdered slate, precipitated calcium silicates, precipitated aluminum silicates, precipitated calcium aluminum silicates, precipitated sodium aluminum silicates, feldspars, mullite, silicas such as quartz, fused silica, cristobalite, diatomaceous earth, siliceous earth, precipitated silica, pumice powder, perlite, calcium metasilicate, fibers from melts of glass or basalts, glass powder, glass beads, and slags. Barium sulfate and/or talc can, for example, be used as fillers.

In an embodiment of the present invention, the coating materials can, for example, contain up to 50, for example, 0.00001 to 40, for example, 0.00001 to 30 wt. % aprotic solvents, wherein the indicated amounts respectively relate to the total amount of the coating material. The expression “aprotic solvents” is understood in the following to refer to solvents that contain no ionisable protons in the molecule. Suitable aprotic solvents are, for example, aliphatic hydrocarbons, cycloaliphatic hydrocarbons, aromatic hydrocarbons, ketones, esters, ethers, ether esters, in particular, ethylacetate, butyl acetate, acetone, n-butanone, methyl isobutyl ketone, methoxypropyl acetate, and dimethyl sulfoxide. Ethylacetate, butyl acetate, acetone, n-butanone, methyl isobutyl ketone, methoxypropyl acetate, and mixtures thereof, can, for example, be used as solvents.

The compounds used as catalysts C according to the present invention are latent bases, as the carbonate salt according to Formula II is in equilibrium with its disassociation products, carbon dioxide and the corresponding hydroxide- or alkoxy base. As long as carbon monoxide cannot escape from the system, the equilibrium lies more strongly in favor of the carbonate salt. Only when a carbon dioxide is removed, and thus a sufficient amount of base is present, does the cross-linking begin with the aid of the Michael addition. With regard to storage of the coating materials according to the present invention in closed containers, from which carbon dioxide cannot escape, the coating material may basically be formulated as a single component system. The shelf life can, however, be increased if the individual components of the coating material according to the present invention are formulated in multicomponent systems. A catalyst component which contains the catalysts C is thus, for example, only mixed shortly before processing with the binder components which contain the CH acidic compounds A and the vinylogous carbonyl compounds B.

According to the present invention, the CH acidic compounds A and the vinylogous carbonyl compounds B may be contained in a binder component together with the light stabilizers, open time extenders, and pot life extenders used. This binder component may additionally contain pigments, other additives, and solvents. The catalysts C and, if necessary, additional solvents and pot life extenders, may be contained in a catalyst component. In an embodiment, the CH acidic compounds A can, for example, be present in a first binder component, the vinylogous carbonyl compounds B in a second binder component, and the catalysts C in a catalyst component. In one such three-component system, the CH acidic compounds A are contained in the first binder component together with the open time extenders and light stabilizers. If necessary, this first binder component may additionally contain pigments and fillers, and additional additives. The vinylogous carbonyl compounds B can, for example, be contained in the second binder component. The second binder component may also contain pigments, fillers, and additional additives. The catalysts C are contained in the catalyst component. The catalyst component may also contain solvents and pot life extenders.

The addition of additional components which are customary for producing a coating reduces the shelf life of RMA systems. The coating materials according to the present invention with their particular selection of light stabilizers, open time extenders, pot life extenders, pigments, dispersing agents, functional fillers, and aprotic solvents have an unexpectedly high shelf life compared to previously known coating materials based on RMA systems.

The properties of coatings which are produced from coating materials based on RMA systems are furthermore negatively influenced by the presence of other components of the coating material, in contrast to coatings which are produced from coating materials based on conventional binders, for example, epoxy resins or polyurethanes. It has surprisingly been demonstrated that the coating materials according to the present invention result in coatings which have properties necessary for use for components of railway vehicles and aircraft, in particular gloss retention, mechanical stabilities, and light stability.

In an embodiment, the coating materials according to the present invention comprise at least:

-   -   15 to 70, for example, 20 to 60, for example, 25 to 55 wt. % of         CH acidic compounds A, for example, malonic acid esters with         oligomer and polymer substituents based on polyesters, which are         obtained from the reaction of at least malonic acid, malonic         acid dimethyl ester, and/or malonic acid diethyl ester with         hexahydrophthalic acid and/or its anhydride and neopentyl         glycol, and acetoacetic acid esters with oligomer and polymer         substituents based on polyesters, which are obtained from the         reaction of at least acetoacetic acid, acetoacetic acid methyl         ester, and/or acetoacetic acid ethyl ester with         hexahydrophthalic acid and/or its anhydride and neopentyl         glycol;     -   4 to 40, for example, 8 to 35, for example, 10 to 30 wt. %         vinylogous carbonyl compounds B, for example, butanediol         diacrylate, hexanediol diacrylate, trimethylolpropane         triacrylate, pentaerythritol tetraacrylate,         di(trimethylolpropane)tetraacrylate, and/or         dipentaerythritol-hexaacrylate;     -   0.1 to 15, for example, 0.2 to 10, for example, 0.3 to 5 wt. %         catalysts C, for example, tetrabutylammonium methyl carbonate,         tetrabutylammonium ethyl carbonate, tetrabutylammonium hydrogen         carbonate, tetrapropylammonium methyl carbonate,         tetrapropylammonium ethyl carbonate, tetrapropylammonium         hydrogen carbonate, and mixtures thereof;     -   0.00001 to 10, for example, 0.5 to 5, for example, 1 to 3 wt. %         light stabilizers, for example, substituted         2,2,6,6-tetramethylpiperidines, 2-hydroxyphenyltriazines,         2-hydroxybenzophenones, and mixtures thereof;     -   0.00001 to 20, for example, 0.01 to 10, for example, 0.1 to 5         wt. % open time extenders, for example, succinimides,         1,2,4,-triazoles, 1,2,3,-benzotriazoles, and mixtures thereof;     -   0.00001 to 20, for example, 0.01 to 15, for example, 0.1 to 10         wt. % pot life extenders, for example, methanol, ethanol,         n-propanol, i-propanol, n-butanol, i-butanol, and mixtures         thereof; and     -   0 to 50, for example, 0.00001 to 40, for example, 0.00001 to 30         wt. % aprotic solvents, for example, ethylacetate, butyl         acetate, acetone, n-butanone, methyl isobutyl ketone,         methoxypropyl acetate, and mixtures thereof, and

wherein, the indicated amounts respectively relate to the total amount of the coating material.

In an embodiment, the coating materials according to the present invention have at least:

-   -   15 to 70, for example, 20 to 60, for example, 20 to 55 wt. % of         CH acidic compounds A, for example, malonic acid esters with         oligomer and polymer substituents based on polyesters, which are         obtained from the reaction of at least malonic acid, malonic         acid dimethyl ester, and/or malonic acid diethyl ester with         hexahydrophthalic acid and/or its anhydride and neopentyl         glycol, and acetoacetic acid esters with oligomer and polymer         substituents based on polyesters, which are obtained from the         reaction of at least acetoacetic acid, acetoacetic acid methyl         ester, and/or acetoacetic acid ethyl ester with         hexahydrophthalic acid and/or its anhydride and neopentyl         glycol;     -   4 to 40, for example, 8 to 35, for example, 10 to 30 wt. %         vinylogous carbonyl compounds B, for example, butanediol         diacrylate, hexanediol diacrylate, trimethylolpropane         triacrylate, pentaerythritol tetraacrylate,         di(trimethylolpropane)tetraacrylate, and/or         dipentaerythritol-hexaacrylate;     -   0.1 to 15, for example, 0.2 to 10, for example, 0.3 to 5 wt. %         catalysts C, for example, tetrabutylammonium methyl carbonate,         tetrabutylammonium ethyl carbonate, tetrabutylammonium hydrogen         carbonate, tetrapropylammonium methyl carbonate,         tetrapropylammonium ethyl carbonate, tetrapropylammonium         hydrogen carbonate, and mixtures thereof;     -   0.00001 to 10, for example, 0.5 to 5, for example, 1 to 3 wt. %         light stabilizers, for example, substituted         2,2,6,6-tetramethylpiperidines, 2-hydroxyphenyltriazines,         2-hydroxybenzophenones, and mixtures thereof;     -   0.00001 to 20, for example, 0.01 to 10, for example, 0.1 to 5         wt. % open time extenders, for example, succinimides,         1,2,4,-triazoles, 1,2,3,-benzotriazoles, and mixtures thereof;     -   0.00001 to 20, for example, 0.01 to 15, for example, 0.1 to 10         wt. % pot life extenders, for example, methanol, ethanol,         n-propanol, i-propanol, n-butanol, i-butanol, and mixtures         thereof;     -   0 to 70, for example, 0.00001 to 65, for example, 0.00001 to 40         wt. % inorganic and/or organic pigments, for example, titanium         dioxide, iron oxides, carbon blacks, pigment yellow 151, pigment         orange 67, pigment red 170, pigment violet 19, pigment blue         15:3, pigment green 7, and mixtures thereof;     -   0 to 25, for example, 0.00001 to 8, for example, 0.00001 to 5         wt. % dispersing additives, for example, high molecular weight         block copolymers with pigment affinic groups;     -   0 to 60, for example, 0.00001 to 40, for example, 0.00001 to 30         wt. % functional fillers, for example, barium sulfate and/or         talc; and     -   0 to 50, for example, 0.00001 to 40, for example, 0.00001 to 30         wt. % aprotic solvents, for example, ethylacetate, butyl         acetate, acetone, n-butanone, methyl isobutyl ketone,         methoxypropyl acetate, and mixtures thereof,

wherein, the indicated amounts respectively relate to the total amount of the coating material.

The coating materials according to the present invention may be used to produce coating systems which have a structure made from two or more coatings. The coating materials according to the present invention may thereby be used to produce at least one layer or coating. In an embodiment, the coating materials can, for example, be used to produce a two-layer structure; they can, for example, be used to construct a base coat-clear coat system. In the following, coating materials and coatings which contain no coloring agents, are designated as “clear coats”. In the following, coating materials and coatings which contain coloring agents, for example, dyes or pigments, are designated as “base coats”. Base coat-clear coat systems are also often used for aircraft and rail vehicles as they are very weather resistant, primarily with respect to gloss retention.

The coating materials according to the present invention have a surprisingly higher shelf life compared to previously known RMA coating materials and coatings. They also show improved drying behavior. Coatings obtained from the coating materials according to the present invention additionally have an improved light stability, in particular less yellowing and higher gloss retention.

The coating materials according to the present invention have pot lives greater than or equal to 1 hour, for example, greater than or equal to 2 hours, for example, between 2 and 4 hours. The pot life is generally determined via the flow time from a flow cup. The end of the pot life is determined as the point at which the flow time shows double the value of the starting flow time. The testing method is described below in detail in the Examples. The coating materials according to the present invention also demonstrate open times of greater than or equal to 15 minutes, for example, greater than or equal to 20 minutes, for example, greater than or equal to 25 minutes. In addition to the long pot lives and open times, the coating materials according to the present invention surprisingly demonstrate an unusually broad climate window in which they may be processed without deterioration. They are processable, for example, at temperatures up to 45° C. and at relative air humidity of up to 99%. They also demonstrate a long overspray absorption, for example, over a time interval of more than 25 minutes.

In contrast to conventionally used coating materials based on polyurethane, the coating materials according to the present invention have significantly reduced drying times. The coatings according to the present invention may also be masked more quickly, i.e., they are already cured at room temperature 1 to 4 hours after application to the extent that, for example, pattern stencils may be applied which are removed again after painting the pattern without damaging the coating. Glued on stencils are conventionally used to apply color decorations and patterns to a coating.

Due to their properties, the coating materials according to the present invention are suitable primarily for a use for coating large components. They are in particular suitable for coating large surface area components as they are used, for example, in rail car construction and aircraft construction.

The present invention also relates to a method for coating components. The method according to the present invention thereby comprises the steps: (a) applying the coating material according to the present invention to a surface of a substrate; and, (b) curing the applied coating material for 1 to 12, for example, 1 to 6, for example, 1 to 4 hours at temperatures between 5 and 45, for example, 15 and 40, for example, 20 and 35° C.

The coating materials according to the present invention have an above-average high solids content and correspondingly contain low proportions of volatile organic substances, for example, solvents. The solids content is defined as the proportion by mass of a coating material that remains as residue after 30 minutes during evaporation at 105° C. Essentially, the solids generally comprise binders, non-volatile additives, pigments, and fillers. The solids content of the coating materials according to the present invention lie between 65 and 95, for example, 70 and 90, for example, between 75 and 85 wt. %, relative to the total weight of the coating materials.

Coating materials with high solids contents are usually poorly processable using conventional spraying methods. In contrast, the coating materials according to the present invention are easily applied with the aid of hydraulic very high pressure spraying (airless), airless spraying with air support (airmix), and with the aid of pneumatic spraying or compressed air spraying. High quality surfaces are surprisingly obtained even using these application methods. Electrostatically supported airspray or airmix methods are particularly suitable according to the present invention.

Suitable substrates are metals, for example, aluminum, aluminum alloys, steels, and iron alloys, plastic materials, and glass- and carbon fiber reinforced fiber composite materials. The component surfaces to be coated may be provided with a primer, for example, the conventional primers known to the person skilled in the art based on epoxy resins or polyurethanes.

In the case of coating materials according to the present invention which have multiple components, all components are mixed prior to the application. The mixing may thereby be carried out manually or by machine. In an embodiment, a coating system may be produced with at least one additional coating, where additional coating materials are applied and cured on the first coating.

In an embodiment of the method according to the present invention, a coating system is produced in a two-layer structure. First, a base coat is applied and cured; then, a clear coat is applied thereon and cured. The base coat or the clear coat or both the base and clear coats may be produced from coating materials according to the present invention.

The coatings according to the present invention have a dry coating thickness of 20 through 150 μm. Low coating thicknesses that still have high opacity are suitable, in particular, for coating components for aerospace, as weight may thus be saved.

As the coating materials according to the present invention may be cured at room temperature, they are primarily suitable for coating large components, as they are used, for example, to build aircraft and railway cars. They are suitable in particular for the coating of fuselages, wings, radomes, vertical fins, elevators, engine claddings, winglets, and landing flaps, and also for driving units, rail car parts, roofs, doors, and chassis linings. They are also suitable for coating interior components of rail vehicles and aircraft, for example, ceiling panels, wall claddings, floor panels, luggage compartment covers, and doors.

EXAMPLES

The production of the coating materials is carried out according to coating technology standards, which are known and familiar to the person skilled in the art. The catalyst solution used in Example Recipes 1 and 2 is produced in that 42.8 g diethyl carbonate and 26.1 g i-propanol are added to a solution of 17.1 g tetrabutyl ammonium hydroxide in 14 g water.

Example Recipe 1 Clear Coat

Amount Substance [wt. %] Filler component Malonate functional polyester with a concentration of acidic 52 protons of 5.66 mol/kg relative to the solvent-free polyester, 85% in butyl acetate. Di(trimethylolpropane)tetraacrylate 23 Hexanediol diacrylate 5.5 Bis(1,2,2,6,6-pentamethyl-4-piperidinyl)-sebacate 3 Succinimide 1.5 Methyl ethyl ketone 6 Catalyst component Catalyst solution 6 Isopropanol 3

Example Recipe 2 Base Coat

Amount Substance [wt. %] Filler component 1 Malonate functional polyester with a concentration of acidic 31 protons of 5.66 mol/kg relative to the solvent-free polyester, 85% in butyl acetate. Titanium dioxide 35 High molecular weight block copolymer with pigment affinic 1 groups Bis(1,2,2,6,6-pentamethyl-4-piperidinyl)-sebacate 1 Succinimide 1 Butyl acetate 4.5 Filler component 2 Di(trimethylolpropane)tetraacrylate 14 Hexanediol diacrylate 3 Catalyst component Catalyst solution 3.5 Isopropanol 2 Methyl ethyl ketone 4

The pot life and the drying time of Example Recipe 2 were determined to evaluate the shelf life of the coating materials according to the present invention. Samples were thereby tested or used to produce a coating after 1 day of storage at 23° C., after 28 days of storage at 40° C., and after 1 year of storage at 20 through 23° C., respectively.

Determination of pot life: The pot life was determined using a flow cup. In this method, a liquid is filled into a cup with a defined volume, which has a defined nozzle in its bottom. The coating material runs out through the nozzle, wherein the time from the discharge of the liquid jet up until the liquid jet breaks off is measured as the flow time. All preparations and measurements are carried out at a temperature of 23° C. Initially, all components of the coating material are mixed and the flow time of the mixture is immediately measured (initial flow time). The measurement is repeated at regular intervals. The end of the pot life is reached when the flow time is double the initial flow time.

Determination of drying time: To determine the drying time, a drying time recorder, a drying time measurement device from BYK Gardner, was used. For this purpose, the coating material to be examined is uniformly applied on glass strips with the aid of a film drawer. The glass strips are subsequently laid in a linear recorder. Needles are then applied to the coating and drawn across the drying film at a defined, constant speed. A characteristic drying image of the coating is thereby created, in which the individual time segments show the different curing states: flow or open time, initial trace, film tearing, and surface track. The curing of the coating material thereby begins at the end of the open time, i.e., at the point at which the track etched by the needle remains visible in the applied film. It ends with the surface track, i.e., at the time at which the needle no longer leaves a visible track in the applied film.

The properties of the coatings which are produced from the differently stored coating materials from Example Recipe 2 were also examined to determine the shelf life of the coating material. For this purpose, gloss and elongation at break were determined. Samples were used to produce a coating after 1 day of storage at 23° C., after 28 days of storage at 40° C., and after 1 year of storage at 20 through 23° C., respectively. To produce the sample bodies, Example Recipe 2 was applied to primed aluminum plates using cup guns and cured at room temperature.

Determination of surface gloss: The gloss of the coating surface was determined as a reflectometer value. The reflectometer value of a sample is defined as the ratio of the light beams reflected by the sample surface and a glass surface with a refractive index of 1.567 in the mirror direction. The measurement values are determined with the aid of a conventional refractometer at an angle of 60°.

Determination of elongation at break: The elongation at break was determined using the cylindrical mandrel bend test. The sample bodies are bent around a mandrel for this purpose. The smaller the radius of the mandrel, around which the plate may be bent without damaging or breaking the coating, the greater the elongation at break of the coating. The diameter of the mandrel is indicated as the measured value.

TABLE Shelf life of Example Recipe 2 1 day, 28 days, 1 year, Storage 24° C. 40° C. 20-23° C. Pot life 2.5 h 2.5 h 2.5 h Open time 59 min 60 min 56 min Surface track ends 136 min 132 min 128 min Elongation at rupture 12 mm 12 mm 12 mm Gloss 87 88 87

As the table shows, the coating materials according to the present invention have a high shelf life. After longer storage at increased temperatures, the coating materials themselves do not demonstrate a deterioration in their processability. The coatings produced therefrom also show no impairment to their properties.

The present invention is not limited to embodiments described herein; reference should be had to the appended claims. 

What is claimed is: 1-25. (canceled)
 26. A coating material for producing a coating, the coating material comprising: 15 to 70 wt. % of at least one CH acidic compound; 4 to 40 wt. % of at least one vinylogous carbonyl compound; 0.1 to 15 wt. % of at least one latent-basic catalyst; 0.00001 to 10 wt. % of at least one light stabilizer; 0.00001 to 20 wt. % of at least one open time extender; and 0.00001 to 20 wt. % of at least one pot life extender, wherein, each wt. % of a respective ingredient is based on a total amount of the coating material.
 27. The coating materials as recited in claim 26, further comprising: up to 70 wt. % of at least one of an inorganic pigment and an organic pigment.
 28. The coating material as recited in claim 27, wherein the at least one of an inorganic pigment and an organic pigment is selected from a titanium dioxide, an iron oxide, a chromium oxide, a chromium titanate, a bismuth vanadate, cobalt blue, a carbon black, pigment yellow 151, pigment yellow 213, pigment yellow 83, pigment orange 67, pigment orange 62, pigment orange 36, pigment red 170, pigment violet 19, pigment violet 23, pigment blue 15:3, pigment blue 15:6, and pigment green
 7. 29. The coating material as recited in claim 26, wherein the at least one CH acidic compound is a compound of the formula

wherein, R is hydrogen, an alkyl radical, or an aryl radical, Y is an alkyl radical, an aralkyl radical, an aryl radical, an alkoxy radical, or an amino group, and Y′ is an alkyl radical, an aralkyl radical, an aryl radical, an alkoxy radical, or an amino group.
 30. The coating material as recited in claim 26, wherein the at least one vinylogous compound is at least one of an acrylate and a maleate.
 31. The coating material as recited in claim 26, wherein the at least one latent- basic catalyst is a substituted carboxylic acid salt of the formula

wherein, R is hydrogen, an alkyl radical, an aralkyl radical, or a polymer radical, X⁺ is an alkali earth metal cation, an alkaline earth metal cation, a quaternary ammonium salt of the formula (R′)4Y⁺, or a phosphonium salt of the formula (R′)4Y⁺, wherein, Y is nitrogen or phosphorus, R′ is the same or different, is hydrogen, an alkyl radical, an aral radical, an aralkyl radical, or a polymer, and R and R′ form a ring structure or are a polymer.
 32. The coating material as recited in claim 26, wherein the at least one light stabilizer is selected from a radial scavenger, a UV absorber, a quencher, and a peroxide decomposer.
 33. The coating material as recited in claim 26, wherein the at least one pot life extender is selected from an alcohol comprising up to 6 carbon atoms and an evaporation number below
 35. 34. The coating material as recited in claim 26, wherein the at least one open time extender is selected from a basic NH-functional compound with a pK_(a) value of between 4 and
 14. 35. The coating material as recited in claim 26, further comprising: up to 25 wt. % of at least one dispersing additive.
 36. The coating material as recited in claim 35, wherein the at least one dispersing additive is selected from a high molecular weight block copolymer with pigment affinic groups, a highly-branched polyester, and an acrylate polyester copolymer with pigment affinic groups.
 37. The coating material as recited in claim 26, further comprising: up to 60 wt. % of at least one functional filler.
 38. The coating material as recited in claim 37, wherein the at least one functional filler is selected from a carbonate, a sulfate, a silicate, and a silica.
 39. The coating material as recited in claim 26, further comprising: up to 50 wt. % of at least one aprotic solvent.
 40. The coating material as recited in claim 39, wherein the at least one aprotic solvent is selected from an aliphatic hydrocarbon, a cycloaliphatic hydrocarbon, an aromatic hydrocarbon, a ketone, an ester, an ether, and an ether ester.
 41. A method of using the coating material as recited in claim 26 in a coating system, the method comprising: providing the coating material as recited in claim 26; and incorporating the coating material so as to provide at least one coating in the coating system.
 42. The method as recited in claim 41, wherein the at least one coating in the coating system is at least one base coat.
 43. The method as recited in claim 41, wherein the at least one coating in the coating system is at least one clear coat.
 44. A method for coating a component, the method comprising: applying the coating material as recited in claim 26 to a substrate; and curing the coating material for 1 to 12 hours at a temperature of between 5 and 45° C.
 45. The method as recited in claim 44, wherein the applying of the coating material is performed by a spraying method.
 46. The method as recited in claim 44, further comprising: mixing the respective ingredients of the coating material prior to applying the coating material.
 47. A component comprising a coating produced from the coating material as recited in claim
 26. 48. The component as recited in claim 49, wherein the component is a rail vehicle component or an aircraft component. 